Introduction
WQ-E540 is water-based polytetrafluoroethylene wax dispersion.
Physical Property
| Properties | Units | Values |
| Appearance | --- | White to yellowish liquid |
| Solid type | --- | PTFE wax |
| Solid Content | % | 46±1 |
| Lonicity | --- | Anionic |
| pH value | --- | 7.0-9.0 |
| Melting point | ℃ | 320 |
Performance
Excellent abrasion resistance and scratch resistance
Excellent good slippery, anti-blocking
Application
Adding into water based paints, inks, and water based finishing agent, it offers the coating film a very low coefficient of friction, excellent slip and scratch resistance.
It can be used in water-based industrial (metal) coatings to reduce the friction coefficient of the coating film and enhance the wear resistance and scratch resistance of the coating.
Usage
It is recommended to add the wax emulsion at the end of the mixing process, while stirring.
The recommended amount of wax emulsion to be added is between 1 and 5%.
To ensure uniformity, please shake well before use.
When mixing with other materials, please test the suitability firstly, especially considering the pH value.
Package
Packed in 200Kg/barrel, 1000KGS IBC.
Storage
Store in cool, dry and ventilated place.
The shelf life of the original packaging is 12 months at room temperature. Once it is opened, it is recommended to use it up soon.
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.